The difference between 3003 and 5052 aluminum plate

Edit: admin Date: 2017-09-11 11:29
3003 aluminum plate and 5052 aluminum plate’s difference in chemical composition, mechanical properties and characteristics.
3003 Aluminum Features:
3003 for the AL-Mn alloy, is the most widely used a rust-proof aluminum, the strength of this alloy is not high (slightly higher than the industrial aluminum), can not heat treatment to strengthen, so the use of cold processing methods to improve its mechanical properties: In the annealing state has a high plasticity, semi-cold hardening when the plastic is still good, cold hardening when the plastic low, good corrosion resistance, good weldability, cutting performance. Uses are mainly used for low load parts requiring high plasticity and good weldability, working in liquid or gaseous media, such as mailboxes, petrol or lubricating oil conduits, various liquid containers and other small load parts made with deep drawing: Wire used to make rivets.
3003 Aluminum chemical composition and characteristics
3003 Aluminum Chemical composition:
Al :margin; Si :0.6; Cu :0.05--0.2; Zn:0.10; Mn:1.0--1.5; Fe:0.7; Single:0.05
3003 aluminum plate mechanical properties
Tensile strength σb (MPa)) 120-160
Conditional yield strength σ0.2 (MPa)) ≥85
Sample size: all wall thickness
Note: longitudinal mechanical properties of pipe at room temperature
Aluminum plate with the national standard (GB / T 3880-2006), applicable to aluminum alloy strip material uniform standards.
5052 aluminum plate characteristics
5052 aluminum’s main alloying elements are magnesium, with good forming processability, corrosion resistance, weldability, medium strength, used in the manufacture of aircraft fuel tanks, tubing, and traffic vehicles, ship's sheet metal parts, instruments, street lamps and rivets, Metal products, electrical and other shells. ② AL-Mn alloy, is the most widely used a rust-proof aluminum, this alloy of high strength, especially with anti-fatigue strength: plasticity and corrosion resistance, can not heat treatment to strengthen, in the semi-cold hardening plastic Still good, cold hardening when the plastic low, good corrosion resistance, good weldability, cutting performance can be poor, can be polished. Uses are mainly used for low load parts requiring high plasticity and good weldability, working in liquid or gaseous media such as fuel tanks, petrol or lubricants, various liquid containers and other small load parts made with deep drawing: Wire used to make rivets.
Chemical composition and properties of aluminum plates
5052 Aluminum Chemical composition:
Al :margin ;Si :0.25;Cu :0.10;Mg:2.2~2.8;Zn:0.10; Mn:0.10;Cr:0.15~0.35 ;Fe: 0.40 
Mechanical properties of aluminum plate
Tensile strength (σb): 170 ~ 305MPa
Conditional yield strength σ0.2 (MPa) ≥65
Elastic modulus (E): 69.3 ~ 70.7Gpa
The annealing temperature was 345 ° C.