In recent years, with the rapid development of the shipbuilding industry at home and abroad, reducing the weight of the hull, increasing the speed of the ship and seeking for the aluminum alloy material instead of the steel parts have become an important subject of aluminum processing industry and shipbuilding industry. 6082 aluminum plate has medium strength, good corrosion resistance, light weight, with the improvement of research and develop level, 6082 aluminum plate will usher in another peak of production and sales.

The superior performance of 6082 aluminum plate comes from the precise requirements of its production process. For example, Henan Mingtai Aluminum, the top 10 aluminum processing company in China, has a well-known 6082 aluminum plate in the domestic aluminum plate market due to its strict technology, superior performance and reliable quality.
The production and control of 6082 alloy aluminum plate in Mingtai Aluminium is extremely accurate. The first is melting, 6082 aluminum plate is characterized by Mn, Mn is refractory metal. The melting temperature should be controlled at 740 - 760 ℃. Before sampling, stirring should be done more than twice to ensure the metal is completely melted, with accurate temperature and uniform composition.In the middle of the depth of molten aluminum, a sample is taken from each side of the furnace for analysis, the points after passing the converter. The second is purification and casting process. After the melt is transferred to the static furnace, the powder is sprayed with nitrogen and refining agent, the refining temperature is 735-745 ℃, the time is 15 minutes, and the refining time is 30 minutes.Through the process of degassing, slag removal, purification of the melt. During casting, there are two filtration devices between the mold and the mouth of the furnace. There are foam ceramic filter plates (30PPI) at the mouth of the furnace. Before filtration, they are filtered through a 14-mesh glass fiber cloth and filtered to remove oxide and slag in the melt.
"6082 aluminum alloy casting temperature is too high, casting speed is low, the water flow is too large, the above-mentioned process should be strictly controlled." said the responsible person of Mingtai Aluminium. Because of such a strict requirement, it has created the Mingtai Aluminum brand long-term Reputation.